High Temperature Plastic Teflon Ptfe Sheet White With Graphite Carbon Bronze Filling
Product number:High Temperature Plastic Teflon Ptfe Sheet White With Graphite Carbon Bronze Filling
Quick Overview: Place of Origin: China (Mainland) Certification: SGS,IOS9001,ISO14001
Send Inquiry
PDF DownLoad
Product Description
PTFE skived Sheet is manufactured by technique of compacting, sintering, rotary cutting with PTFE granular resin. It has good dielectric performance and non-aging, best anti chemistry corrosion ability and wide applying intension range.
PTFE molded shet is manufactured by molding process with PTFE regular resin and sintering.It is very suitable for seals,lining,diaphragm,spacer guide and bearing pad for bridge.
PTFE SHEET
|
ITEM |
Result |
Unit |
|
Material |
100% Virgin PTFE |
|
|
Apparent density |
2.10-2.30 |
g/ cm3 |
|
Tensile Strength |
22-28 |
Mpa |
|
Ultimate Elongation |
250-300 |
% |
|
Dielectric Strength |
40 |
KV/mm |
|
Tempature Resist |
-180-+260 |
oC |
|
PTFE Molded sheet Thickness |
1.5mm-----120mm |
|
|
Molded sheet Length * width |
Min Dimension=300x300mm, Max Dimension= 2000x2000mm Other sizes based on your requirements |
|
|
PTFE Skived sheet thickness |
0.1mm-----10.0mm |
|
|
PTFE Skived sheet width(Max) |
2700mm |
|
Main Features
1.Heat resistance property---It is able to wok stably between -180°C to +260°C.
2.Excellent non-sticky property---It easier to remove those resin, dopes, oil and other sticky things.
3.Good mechanical property with no distortion and low friction coefficient.
4.Excellent insulation property.
5.Materials like carbon, graphite and glass fiber can be filled.
6.Virgin and recycled materials are available
Main properties
|
Properties |
Unit |
Result |
|
Apparent density |
g/cm3 |
2.10-2.20 |
|
Tensile strength (min) |
MPa |
20 |
|
Ultimate elongation (min) |
% |
200 |
|
Residual Lubricant Content (max) |
% |
0.5 |
|
Dialectric Strength (min) |
KV/mm |
10 |
Details
PTFE resin,filled with some filling stuff,can prolong the life of
products and strengthen the performance,eg:Graphite,Carbon ,Glass fiber
,bronze
|
Glass Fiber: |
Increases compressive strength, rigidity and wear. |
|
Carbon: |
Increases compressive strength, hardness, wear, and load properties. |
|
Graphite: |
Reduces coefficient of friction |
|
Molybdenum Disulfide: |
Increases hardness, stiffness, and wear |
|
Bronze: |
Increases hardness and wear resistance |